性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 比重 | ASTM D-792 | 1.06 | 23/23℃ | |
熔体流动速率 | 220℃×10kg | ASTM D-1238 | 6.0 | g/10min | |
机械性能 | 弯曲弹性率 | ASTM D-790 | 2.5×104 | kg/cm2 | |
伸长率 | ASTM D-638 | 15 | % | ||
弯曲弹性率 | ASTM D-790 | 3.5×105 | lb/in2 | ||
弯曲强度 | ASTM D-790 | 750 | kg/cm2 | ||
弯曲强度 | ASTM D-790 | 10630 | lb/in2 | ||
引张强度 | ASTM D-638 | 440 | kg/cm2 | ||
IZOD冲击强度 | 1/4〃 | ASTM D-256 | 14 | kg.cm/cm | |
引张强度 | ASTM D-638 | 6240 | lb/in2 | ||
IZOD冲击强度 | 1/8" | ASTM D-256 | 17 | kg.cm/cm | |
洛氏硬度 | ASTM D-785 | 115 | R | ||
IZOD冲击强度 | 1/8" | ASTM D-256 | 3.2 | ft.lb/in | |
IZOD冲击强度 | 1/4〃 | ASTM D-256 | 2.6 | ft.lb/in | |
热性能 | 热变形温度 | ASTM D-648 | 105(221) | ℉ | |
热变形温度 | ASTM D-648 | 115(239) | ℃ | ||
维卡软化点 | ASTM D-1525 | 125 | ℃ | ||
燃烧性 | File No. E56070 UL&C-UL | 1/16"HB | |||
维卡软化点 | ASTM D-1525 | 257 | ℉ |